What is the way to prevent high-flex cable core breaks?
Times：May 3,2019 Hits：807
The non-standard manufacturing of high-flexible cables can lead to core breakage. If a high-flex cable needs to be replaced immediately after a broken core, what is the way to prevent the high-flex cable core from breaking? Let's take a look at it below.
The non-standard manufacturing of high-flexible cables can lead to core breakage. If a high-flex cable needs to be replaced immediately after a broken core, what is the way to prevent the high-flex cable core from breaking? Let's take a look at it below.
What is the way to prevent high-flex cable core breaks?
1. Shield production process
Mainly due to the wrong handling method of the copper wire joint when the high-flexible cable is woven or wound; the anti-twisting function of the high-flexible cable is insufficient, so that the excessively intense distortion occurs, and the braid layer is twisted by itself.
2. Unqualified raw material selection
The functions of high-flexible cables produced by different raw materials are different. For example, in certain environments, it is required to have low temperature resistance, UV resistance, oil resistance, etc. These have certain requirements for the performance of the outer sheath, and the outer sheath is resistant. If it is abrasive, it will not cause adhesion. The thicker the jacket, the slower the heat dissipation, so improper selection of the jacket is likely to lead to core breakage.
3, the outer sheath is damaged
The damage of the outer sheath is related to the material and performance of the production. However, if the user operates improperly, the probability of occurrence of heat and insulation breakdown of the conductor will be greatly increased, which is also the main reason for the broken core of the towline cable. Therefore, the manufacture of the towline cable must ensure quality clearance.
4, the conductor specifications do not meet the specifications
Generally speaking, the thinner the conductor, the better the flexibility of the cable. However, if the conductor is too thin, the possibility of the cable being entangled during use is greatly increased. In the long run, the hardness may be insufficient, the material may be worn, or even the fracture may occur. .
The above is the introduction of the reason why the high-flex cable core breaks, I hope to help everyone.